Oleh : Yusmar Palapa Wijaya, Khairul Anuar Mohamad, Abu Bakar Abdul Rahman, Afishah Alias, Mohammad Syahmi Nordin, Telkomnika
Dibuat : 2021-09-10, dengan 0 file

Keyword : perovskite, RF magnetron sputtering, SrSnO3, strontium stannate, thin film
Url : http://journal.uad.ac.id/index.php/TELKOMNIKA/article/view/18790
Sumber pengambilan dokumen : Web

This paper presents physical and morphology properties of strontium stannate (SrSnO3) perovskite-type as a candidate of an n-type material thin film for organic-inorganic hybrid diode heterojunction for optoelectronics application. Typical wet-process of SrSnO3 deposition produce thick film and having 10-8 S/cm order in conductivity. The SrSnO3 thin films were deposited on ITO glass substrates by RF magnetron sputtering using a purity 99.9% SrSnO3 target with 5.0 mTorr of gas pressure and 100 W of RF power at room temperature. The gas composition of pure argon (75%) and reactive oxygen gas (25%) was used for 60 min. XRD diffraction patterns revealed that the thin films are orthorhombic crystal structure with lattice parameter a=5.7040 Ǻ, b=8.06 Ǻ and c=5.7080 Ǻ with a strong orientation in the (002) direction. SEM images showed that films exhibited uniform surface morphology with a roughness average of Ra=2.258 nm and thickness of 311 nm. The EDX spectrum confirmed the presence of O, Sr, and Sn elements in the films with 75.22%, 8.29%, 16.49% in atomic number, respectively. The films were having a conductivity of 8.33x102 S/cm with low resistivity of 12.4x10-3W-cm.

Deskripsi Alternatif :

This paper presents physical and morphology properties of strontium stannate (SrSnO3) perovskite-type as a candidate of an n-type material thin film for organic-inorganic hybrid diode heterojunction for optoelectronics application. Typical wet-process of SrSnO3 deposition produce thick film and having 10-8 S/cm order in conductivity. The SrSnO3 thin films were deposited on ITO glass substrates by RF magnetron sputtering using a purity 99.9% SrSnO3 target with 5.0 mTorr of gas pressure and 100 W of RF power at room temperature. The gas composition of pure argon (75%) and reactive oxygen gas (25%) was used for 60 min. XRD diffraction patterns revealed that the thin films are orthorhombic crystal structure with lattice parameter a=5.7040 Ǻ, b=8.06 Ǻ and c=5.7080 Ǻ with a strong orientation in the (002) direction. SEM images showed that films exhibited uniform surface morphology with a roughness average of Ra=2.258 nm and thickness of 311 nm. The EDX spectrum confirmed the presence of O, Sr, and Sn elements in the films with 75.22%, 8.29%, 16.49% in atomic number, respectively. The films were having a conductivity of 8.33x102 S/cm with low resistivity of 12.4x10-3W-cm.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	gdlhub
Organisasi	Telkomnika
Nama Kontak	Herti Yani, S.Kom
Alamat	Jln. Jenderal Sudirman
Kota	Jambi
Daerah	Jambi
Negara	Indonesia
Telepon	0741-35095
Fax	0741-35093
E-mail Administrator	elibrarystikom@gmail.com
E-mail CKO	elibrarystikom@gmail.com