Oleh : Fadliondi Fadliondi, Muhammad Kunta Biddinika, Shun-ichiro Ohmi, Telkomnika
Dibuat : 2017-06-12, dengan 1 file

Keyword : pentacene;semiconductor;organic;electronics;transistor
Url : http://journal.uad.ac.id/index.php/TELKOMNIKA/article/view/5834
Sumber pengambilan dokumen : web

Metal-oxide-semiconductor field-effect transistors (MOSFET) were fabricated using organic semiconductor pentacene. The humidity dependence of drain current gate voltage (ID-VG) characteristic and drain current drain voltage characteristic (ID-VD) will be explained. Firstly, the thermal oxidation method was used to grow SiO2 gate insulator with thickness of 11 nm. Secondly, the thermal evaporation method was used to form Au source and drain electrodes with thickness of 28 nm. The channel width and length of the transistors were 500 mm and 200 mm, respectively. By the same method, organic semiconductor material pentacene was deposited with thickness of 50 nm at vacuum of 7.8x10-6 Torr. The hole mobility decreased from 0.035 cm2/(Vs) to 0.006 cm2/(Vs), while the threshold voltage increased from 0.5 V to 2.5 V and gate leakage current also increased from 5.8x10-10 A to 3.3x10-9 A when the relative humidity increased from 20% to 70%.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	gdlhub
Organisasi	Telkomnika
Nama Kontak	Herti Yani, S.Kom
Alamat	Jln. Jenderal Sudirman
Kota	Jambi
Daerah	Jambi
Negara	Indonesia
Telepon	0741-35095
Fax	0741-35093
E-mail Administrator	elibrarystikom@gmail.com
E-mail CKO	elibrarystikom@gmail.com